Emulated wood with pores and fibers and fabrication method thereof

ABSTRACT

A method for fabricating emulated wood with pores and fibers, comprising: immersing a plurality of synthetic fibers configured parallel in a plane into a resin so that the resin is coated on the surfaces of the plurality of synthetic fibers and in the gaps between the plurality of synthetic fibers; placing the plurality of synthetic fibers between two sheets, wherein the two sheets are planar sheets made from a uniform composition comprising a thermoplastic elastomer, a foaming agent, and a crosslinking agent; carrying out a heat-press process on the two sheets so that the foaming agent undergoes microcellular foaming and forms dense closed pores in the two sheets, and so that the composition on inner surfaces of the two sheets expands towards the plurality of synthetic fibers and penetrates through the gaps between the plurality of synthetic fibers; and cooling the two sheets to yield an emulated wood board.

FIELD OF THE INVENTION

The invention relates to an emulated wood, and more particularly to anemulated wood with pores and fibers fabricated by foaming thermoplasticelastomers so that the emulated wood has not only wood characteristics(non-toxicity, recyclability, good dyeability, weather resistance, etc.)and wood grain of genuine wood, but also plasticity and fiber strengthsuperior to those of genuine wood.

BACKGROUND OF THE INVENTION

Among the variety of natural resources, the forest resource is anextremely significant resource of the Earth; in addition to producingdiverse animal and plant ecology, the forest has also provided all kindsof resources required by humans and is closely related to our dailylife. Therefore, the enhancement of the utilization rate, recoveringrate, and recycling rate of wood has been a crucial topic requiringbreakthroughs to be made for countries over the world, so as to reducethe unnecessary wasting of natural resources and effectively reduce themanpower and material resources required for processing scrap. In viewof this, researches in wood-plastic composite (WPC) prepared using woodscraps or particles have received more and more attention in the worldowing to the dimensional stability and insect resistance of WPC beingsuperior to genuine wood in addition to the effective utilization ofwood fiber scraps to fabricate WPC; therefore, WPC may be used for up to25-30 years without particular maintenance. At present, the applicationof WPC is mainly in materials for transportation and non-structural andsemi-structural architectures; for the example of United States, thereare more than thirty WPC outdoor decking manufacturers and the marketshare of WPC outdoor decking has reached about 25%. Such indicates widerand popular utilizations and applications of WPC in the future.

Generally speaking, composite materials combine two or more rawmaterials with different characteristics by different processes toutilize the characteristics and advantages of each of the raw materials,and produce new materials having superior characteristics and satisfyingrequirements by synergistic effects. Among various composite materials,fiber-reinforced composite materials have superior characteristics andwider applications. The composite material is known as a wood-basedcomposite when one of the raw materials is wood, and the fabrication ofwhich mainly uses wood scraps or particles of different sizes to mixwith adhesives and bond into boards under high temperature and highpressure. Conventional wood-based composites commonly useformaldehyde-based adhesives and issues of free formaldehyde often occurduring usage; such wood-based composites also often expand and dispersewhen soaked into water. To solve such issues, wood-plastic composites(WPC) have been produced by mixing wood with plastic raw materials toreduce the release of free formaldehyde and improve the dimensionalstability issues. In addition, since WPC combines the characteristics ofwood and plastic, the shortcomings of each of the two raw materials maybe overcome; for instance, plastic has the disadvantages of highspecific weight, poor antistatic properties, and poor elasticity, yetthe addition of wood reduces the specific weight and enhances antistaticproperties and elasticity; on the other hand, for the wood raw material,the addition of plastic improves the dimensional stability, insectresistance, decay resistance, and weather resistance of the wood.Furthermore, when the percentage of added wood fiber increases, thestructural strength or modulus of elasticity (MOE) of the material alsoincreases.

Conventional WPC are fabricated by mixing wood flour or pulp materialswith typical thermoplastics such as polyethylene, polypropylene,polyvinyl chloride, or polystyrene and form wood-fiber-plastic compositematerials (or wood-flour-plastic composite materials) under hightemperature. At present, approximately 70% of WPC uses polyethylene asthe plastic matrix while lesser parts use polypropylene and polyvinylchloride as the plastic matrix. In addition, to enhance the strength andductility of thermoplastic products and reduce production cost, fibersand fillings are often added to the plastic as intensifiers; most of theearly plastic industries (about 93%) use synthetic fibers for thefibers, while recycled wood fibers have become more common in the recentyears. The oil crisis in the 1970s has also encouraged the usage ofbiomass fibers in the industry.

In summary, WPC substitutes the inorganic fiber materials or fillings inconventional plastics with wood fibers, and when the wood fibers aremixed with thermoplastics to yield composite materials, not only thephysical characteristics and mechanical properties of wood materials areeffectively improved but also the processability is enhanced. Therefore,WPC has largely replaced conventional metal, plastic, and solid woodmaterials in recent years and is commonly applied in products ofdecking, fences, outer panels, frames, and roofs. However, severalissues exist when wood fiber (or wood flour) is used as an intensifieror filling for plastics, and the main issue among which is that thedifference between the surface polarities of plastics and wood fibershinders the chemical bonding between the two; furthermore, wood fiberssuffer from poor dispersion in plastics due to hydrogen bonds betweenthe fibers.

To solve the compatibility issue of plastic and fibers, coupling agentsor adhesion-promoting agents such as maleated polyethylene (MAPE),maleic anhydride grafted polypropylene (MAgPP), and oxidized LDPE may beused to overcome this issue; however, to solve the poor dispersion issueof fibers requires adding dispersing agents such as stearic acid,paraffin wax, or mineral oil to achieve improvements. In addition,grafting may be utilized to form copolymers of monomers (e.g.,1-phenylthene, 4-methyl-2-oxy-3-oxopent-4-ene, etc.) and wood fibers tosolve the issues of fiber polarity and dispersion. Chemical modificationis also used in recent years to improve the interface properties of WPC.Generally speaking, although chemical modification may reduce thesurface polarity of WPC and enhance the compatibility of wood andplastic, it requires using many chemicals, where the most basic chemicalmodification uses modifiers with a single functional group; modifierswith double functional groups or multiple functional groups may also beused. Among various chemical modification methods, the most appreciatedand practical one is the method of reacting acetic anhydride withhydroxyl groups of the wood, i.e., acetylation; however, when carryingout acetylation reactions by acetic anhydride, longer reaction times arerequired to obtain superior weight percentage gain (WPG) or degree ofsubstitution when under environments without solvents and catalysts;therefore, solvents such as dimethylformamide (DMF), dimethyl sulfoxide(DMSO) or pyridine are commonly used when carrying out acetylationreactions by acetic anhydride to enhance the reaction rate with aceticanhydride so that superior acetylation results may be achieved inshorter reaction times. However, the addition of solvents inevitablyincreases cost and toxicity resulting from the solvent, while thereaction time still takes several hours to achieve a superioracetylation result.

The rising environmental consciousness in recent years has impeded thepopular usage or application of the aforementioned WPC or other plasticcomposites in our daily needs due to the various structuraldisadvantages and toxicity issues described in above. Thusly, thedevelopment of an emulated wood with high elasticity and strength,non-toxicity, recyclability, good dyeability, weather resistance, etc.and further emulating the wood characteristics and wood grain of genuinewood and having plasticity and fiber strength superior to those ofgenuine wood has been a crucial topic to be solved for manufacturersover the world.

BRIEF SUMMARY OF THE INVENTION

An aspect of the invention provides an emulated wood with pores andfibers and a fabrication thereof, the fabrication method comprising:immersing a plurality of synthetic fibers (such as glass fibers orcarbon fibers) configured parallel in a plane into a resin so that theresin is coated on the surfaces of the plurality of synthetic fibers andin the gaps between the plurality of synthetic fibers; placing theplurality of synthetic fibers between two sheets so that the pluralityof synthetic fibers and the two sheets are attached to each other,wherein the two sheets are planar sheets made from a uniform compositioncomprising a thermoplastic elastomer (TPE), a foaming agent, and acrosslinking agent; carrying out a heat-press process on outer surfacesof the two sheets so that the foaming agent in the two sheets undergoesmicrocellular foaming after being heated and forms dense closed pores inthe two sheets, and so that the composition on inner surfaces of the twosheets expands towards the plurality of synthetic fibers and penetratesthrough the gaps between the plurality of synthetic fibers to beintertwined by pressure from microcellular foaming of itself andsurroundings; and cooling the two sheets to yield an emulated woodboard, wherein the inner surfaces of the two sheets after microcellularfoaming form irregular contact surfaces with the plurality of syntheticfibers and are densely and firmly combined in one by adherence force ofthe resin. Since the two sheets not only have high elasticity andstrength of rubber but also have advantages of non-toxicity,recyclability, good dyeability, weather resistance, etc., the two sheetsmay emulate the wood characteristics and wood grain of genuine woodafter dyeing and foaming and forming dense closed pores within. Inaddition, since the inner surfaces of the two sheets after microcellularfoaming form irregular contact surfaces with the plurality of syntheticfibers and are densely and firmly combined in one, the resultingemulated wood board has plasticity and fiber strength superior to thoseof genuine wood boards.

Another aspect of the invention provides steps of a rolling processafter the step of yielding an emulated wood board to yield an emulatedwood column, wherein the steps of the rolling process comprise: heatingthe emulated wood board; rolling, with the plurality of synthetic fibersas axes, the emulated wood board densely to attach the outer surface ofan inner sheet of the two sheets to the outer surface of an outer sheetof the two sheets so that the outer surface of the inner sheet and theouter surface of the outer sheet are fused in one after the two sheetsare heated to soften and the outer surfaces of the two sheets aremelted; and cooling the inner sheet and the outer sheet to yield anemulated wood column. Since the plurality of synthetic fibers are alongthe axis of the emulated wood column and is equidistantly or helicallydistributed radially, the emulated wood column has fiber strength farmore superior to that of genuine wood columns and may be easily moldedinto columns with different cross-section shapes.

Another aspect of the invention provides that the composition of the twosheets comprises the thermoplastic elastomer with a weight percentage of10-80%, the crosslinking agent with a weight percentage of 0.01-2.0%,and the foaming agent with a weight percentage of 0.1-15.0%, wherein thetypes and proportions of the thermoplastic elastomer may be adjusted toprepare emulated wood with different properties such as hardness ordensity.

Another aspect of the invention provides that the thermoplasticelastomer at least comprises two thermoplastic elastomers with differentcharacteristics (i.e., a first thermoplastic elastomer and a secondthermoplastic elastomer), wherein the first thermoplastic elastomer is apolymer group of one or any mixture of styrene-butadiene-styrene blockcopolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), andstyrenic block copolymer (SBC) with a weight percentage of 10-80% as amatrix for a soft-segment structure of the two sheets, and wherein thesecond thermoplastic elastomer is a polymer group of one or any mixtureof polystyrene (PS), acrylonitrile-styrene copolymer (AS),acrylonitrile-butadiene-styrene (ABS), and high-impact polystyrene(HIPS) with a weight percentage of 10-80% as a matrix for a hard-segmentstructure of the two sheets. Therefore, the weight percentage of thefirst thermoplastic elastomer or the second thermoplastic elastomer maybe adjusted according to actual needs to adjust the materialcharacteristics of the soft-segment structure and the hard-segmentstructure of the two sheets so as to emulate the different soft and hardwood characteristics of various genuine woods.

Another aspect of the invention provides that the two sheets arefabricated by heating the composition at a temperature above 100° C. tobe softened and melted and mixed into a molten, wherein the molten issubsequently kneaded at a temperature range of 110-130° C. to uniformlymix the composition, wherein the molten is subsequently sheeted by acalendar machine to yield the two sheets, and wherein the thickness ofthe two sheets is between 0.5 and 1.0 mm.

Another aspect of the invention provides that the temperature of theheat-press process is in the range of 160-180° C. and the pressure ofthe heat-press process is in the range of 250-300 kg/cm².

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 is an exploded view of the structure of an emulated wood of theinvention;

FIG. 2 is a flow chart of a fabrication method of the emulated wood ofthe invention;

FIG. 3 is a detailed cross-section view of an emulated wood board of theinvention before completion;

FIG. 4 is a detailed cross-section view of the emulated wood board ofthe invention after completion;

FIG. 5 is a schematic of a finished emulated wood column of theinvention; and

FIG. 6 is a flow chart of a fabrication method of the emulated woodcolumn of the invention.

DETAILED DESCRIPTION OF THE INVENTION

The purposes, processes, structure features, and effects of theinvention may be more fully understood by the subsequent detaileddescription and examples with references made to the accompanyingdrawings.

Commercial thermoplastic elastomers (TPE) are polymers having thecharacteristics of high elasticity and high strength of rubber, and notonly do they have the processability of thermoplastics but they alsohave the physical properties of vulcanized rubber, and thus is acombination of the advantages of plastic and rubber; in addition, thecharacteristics of superior ultraviolet-resistance, weather resistance,and high-temperature resistance renders it suitable for long-termoutdoor applications. Therefore, the applications of TPE have graduallyreplaced those originally of vulcanized rubber. Furthermore, since thefabrication process of TPE usually requires no or short times ofvulcanization, energy may be effectively saved and the generated waste(such as flash or residue) and final rejected products may all berecycled and reused, and even the used TPE products may be recycledafter simple regeneration processes. In short, TPE further hasoutstanding characteristics of reducing environmental pollution andfacilitating resource regeneration.

Among the various commercial TPE materials, styrenic thermoplasticelastomer has properties most close to those of styrene-butadiene rubber(SBR), which is a styrene block copolymer (TPS) of butadiene or isopreneand styrene. The present annual yield of TPS takes up about half of thatof all TPE, and owing to their advantages of material characteristicsstability, non-toxicity, 100% recyclability, and low cost, TPS has beenwidely used in shoe making to replace most rubbers and has increasingapplications in industrial rubber products such as rubber fabric andrubber plates. It is now further used as water-proof membranes for waterproofing and moisture proofing in building roofs, subways, tunnels,trenches, etc. Therefore, the outstanding characteristics of styrenicthermoplastic elastomer in above are utilized to produce an emulatedwood with pores and fibers of the invention after long-term studies soas to fabricate the emulated wood under prerequisites of highavailability and low cost, so that the emulated wood not only hasadvantages of high elasticity and strength, non-toxicity, recyclability,good dyeability, weather resistance, etc. but also emulates the woodcharacteristics and wood grain of genuine wood and has plasticity andfiber strength superior to those of genuine wood.

The invention provides an emulated wood with pores and fibers, thefabrication method of which mainly uses a styrenic thermoplasticelastomer for foaming to emulate the wood characteristics and wood grainof genuine wood and uses synthetic fibers to emulate plasticity andfiber strength superior to those of genuine wood. As shown in FIG. 1, anemulated wood board 10 of the invention comprises at least two sheets 11and 12 and a plurality of synthetic fibers 13 (such as glass fibers orcarbon fibers), wherein the sheets 11 and 12 are made from a compositioncomprising a thermoplastic elastomer, a foaming agent, and acrosslinking agent, wherein the sheets 11 and 12 are fabricated byheating the composition at a temperature above 100° C. to be softenedand melted and mixed into a molten, wherein the molten is subsequentlykneaded at a temperature range of 110-130° C. to uniformly mix thecomposition, wherein the molten is subsequently sheeted by a calendarmachine to yield the sheets 11 and 12, and wherein the thickness of thesheets 11 and 12 is between 0.5 and 1.0 millimeters (mm).

In a preferred embodiment of the invention, to emulate the differentsoft and hard wood characteristics of various genuine woods according toactual requirements, the thermoplastic elastomer at least comprises twothermoplastic elastomers with different characteristics (i.e., a firstthermoplastic elastomer and a second thermoplastic elastomer), whereinthe first thermoplastic elastomer is a polymer group of one or anymixture of styrene-butadiene-styrene block copolymer (SBS),styrene-isoprene-styrene block copolymer (SIS), and styrenic blockcopolymer (SBC) with a weight percentage of 10-80% as a matrix for asoft-segment structure of the two sheets, and wherein the secondthermoplastic elastomer is a polymer group of one or any mixture ofpolystyrene (PS), acrylonitrile-styrene copolymer (AS),acrylonitrile-butadiene-styrene (ABS), and high-impact polystyrene(HIPS) with a weight percentage of 10-80% as a matrix for a hard-segmentstructure of the two sheets. Therefore, the weight percentage of thefirst thermoplastic elastomer or the second thermoplastic elastomer maybe adjusted according to actual needs to adjust the materialcharacteristics of the soft-segment structure and the hard-segmentstructure of the sheets 11 and 12 so as to emulate the different softand hard wood characteristics of various genuine woods.

The foaming agent in the invention may be selected from an azo-basedchemical foaming agent or a baking soda physical foaming agent with aweight percentage of 0.1-15.0%, and the crosslinking agent may beselected from dicumyl peroxide,2,5-(tert-butylperoxide)-2,5-dimethylhexane, or sulfur with a weightpercentage of 0.01-2.0%. As shown in FIG. 2, the fabrication method ofthe emulated wood board 10 comprises the following steps:

Step 201: immersing a plurality of synthetic fibers 13 (such as glassfibers or carbon fibers) configured parallel in a plane into a resin 14so that the resin 14 is coated on the surfaces of the plurality ofsynthetic fibers 13 and in the gaps 131 between the plurality ofsynthetic fibers 13;

Step 202: as shown in FIG. 3, placing the plurality of synthetic fibers13 between the sheets 11 and 12 so that the plurality of syntheticfibers 13 and the sheets 11 and 12 are attached to each other;

Step 203: carrying out a heat-press process by a heat-press machine onthe sheets 11 and 12 and their outer surfaces, wherein the temperatureand the pressure of the heat-press process may be set according to thematerial and thickness of the sheets 11 and 12, wherein the temperatureof the heat-press process may be adjusted to be in the range of 160-180°C. and the pressure of the heat-press process may be adjusted to be inthe range of 250-300 kilograms per square centimeter (kg/cm²), so thatthe foaming agent in the sheets 11 and 12 undergoes microcellularfoaming after being heated and forms dense closed pores B in the sheets11 and 12, and so that the composition on inner surfaces of the sheets11 and 12 expands towards the plurality of synthetic fibers 13 andpenetrates through the gaps 131 between the plurality of syntheticfibers 13 to be intertwined by pressure from microcellular foaming ofitself and surroundings as shown in FIG. 4; and

Step 204: cooling the sheets 11 and 12.

Therefore, as shown in FIG. 4, the inner surfaces of the sheets 11 and12 after microcellular foaming form irregular contact surfaces with theplurality of synthetic fibers 13 and are densely and firmly combined inone by adherence force of the resin 14 to yield the emulated wood board10, which not only emulates the wood characteristics and wood grain ofgenuine wood but also has plasticity and fiber strength superior tothose of genuine wood.

In another preferred embodiment of the invention, steps of a rollingprocess may be carried out on the emulated wood board 10 after yieldingthe emulated wood board 10 to yield an emulated wood column 20 in FIG.5, wherein the steps of the rolling process are shown in FIG. 6 andcomprise:

Step 601: heating the emulated wood board 10;

Step 602: rolling, with the plurality of synthetic fibers 13 as axes,the emulated wood board 10 densely to attach the outer surface of aninner sheet 11 to the outer surface of an outer sheet 12 so that theouter surface of the inner sheet 11 and the outer surface of the outersheet 12 are fused in one after the sheets 11 and 12 are heated tosoften and the outer surfaces of the sheets 11 and 12 are almost melted;and

Step 603: cooling the inner sheet 11 and the outer sheet 12 to yield theemulated wood column 20.

Therefore, after completing the rolling process and cooling, since theplurality of synthetic fibers 13 are along the axis of the emulated woodcolumn 20 and is equidistantly or helically distributed radially and theouter surface of the inner sheet 11 and the outer surface of the outersheet 12 are fused in one, the emulated wood column 20 has fiberstrength far more superior to those of genuine wood columns and may beeasily molded into columns with different cross-section shapes.

In other embodiments of the invention, foaming promoters, dyes, or fireretardants may be added during the fabrication process of the sheets 11and 12 according to actual needs to enhance and promote the propertiesand performances of the emulated woods 10 and 20 comprising the sheets11 and 12; the foaming promoter may have a weight percentage of0.1-10.0%, the dye may be used to adjust the wood color and wood grainof the emulated woods 10 and 20, and the fire retardant may be used toenhance the fire-retarding ability of the emulated woods 10 and 20.

In summary, the emulated woods 10 and 20 fabricated according to theinvention may have not only wood colors adjusted to be very close tothose of genuine wood but also cross sections with wood grains withpatterns like annual rings; in addition, it has been discovered byvarious physical-property tests of the invention that the hardness andsubstance of the emulated woods 10 and 20 are very close to those ofteak wood, yet their weight is lighter than that of teak wood and theymay undertake heavier weights. Furthermore, it has also been discoveredby various physical-property tests and comparisons of the emulated woods10 and 20 and genuine wood or other WPC materials that the emulatedwoods 10 and 20 of the invention have superior nonabsorbent propertiesand are suitable for manufacturing general outdoor products such asbenches or fences, furniture or decorations, toys or blocks, landscapesor woodworking, stationary, models, etc., and have far more longerlifespans and superior strengths than common genuine wood or other WPCmaterials when used under high-temperature or humid outdoor environmentsfor long terms. Moreover, since the emulated woods 10 and 20 of theinvention use the aforementioned polymer materials as matrices and noother toxic solvent or chemical is added during the entire fabricationprocess, the emulated woods 10 and 20 may be completely recycled andreused after simple processing as like general polymer materials afterbeing discarded when no longer usable; therefore, not only thetroublesome processing of disposals and unnecessary wasting of storagespaces may be effectively avoided, the ultimate purpose of energyconservation and carbon reduction and environment resource protectionmay also be easily achieved.

While the invention herein disclosed has been described by means ofspecific embodiments, numerous modifications and variations could bemade thereto by those skilled in the art without departing from thescope of the invention set forth in the claims.

What is claimed is:
 1. An emulated wood with pores and fibers, whereinthe emulated wood includes two sheets (11, 12) and a plurality ofsynthetic fibers (13), the two sheets (11, 12) are planar sheets madefrom a uniform composition comprising a thermoplastic elastomer, afoaming agent and a crosslinking agent, and the plurality of syntheticfibers (13) are attached between the two sheets (11, 12), respectively,and the emulated wood is characterized in that: the plurality ofsynthetic fibers (13) are configured parallel in a plane, a resin iscoated on the surfaces of the plurality of synthetic fibers (13) and inthe gaps (131) between the plurality of synthetic fibers (13), and thetwo sheets (11, 12) are rolled with the plurality of synthetic fibers(13) as axes to attach an inner surface of an inner sheet (11) of thetwo sheets (11, 12) to an outer surface of an outer sheet (12) of thetwo sheets (11, 12) so that the inner surface of the inner sheet (11)and the outer surface of the outer sheet (12) are fused in one to yieldthe emulated wood; wherein after a heat-press process is carried out onthe two sheets (11, 12), the foaming agent in the two sheets (11, 12)undergoes microcellular foaming and forms dense closed pores (B) in thetwo sheets (11, 12) so that, due to heat pressing on the two sheets (11,12) and microcellular foaming, the composition on inner surfaces of thetwo sheets (11, 12) expands towards the plurality of synthetic fibers(13) and penetrates through the gaps (131) between the plurality ofsynthetic fibers to be intertwined by pressure from microcellularfoaming of itself and surroundings, and the inner surfaces of the twosheets (11, 12) form irregular contact surfaces with the plurality ofsynthetic fibers (13) and are densely and firmly combined in one byadherence force of the resin (14) to yield the emulated wood.
 2. Theemulated wood as claimed in claim 1, wherein the thickness of the twosheets (11, 12) is between 0.5 and 1.0 mm.
 3. The emulated wood asclaimed in claim 2, wherein the thermoplastic elastomer is styrenicthermoplastic elastomer.
 4. The emulated wood as claimed in claim 1,wherein the thermoplastic elastomer is styrenic thermoplastic elastomer.5. The emulated wood as claimed in claim 3, wherein the thermoplasticelastomer at least comprises a first thermoplastic elastomer and asecond thermoplastic elastomer, wherein the first thermoplasticelastomer and the second thermoplastic elastomer are two thermoplasticelastomers with different characteristics, and wherein the firstthermoplastic elastomer is a matrix for a soft-segment structure of thetwo sheets (11, 12) and the second thermoplastic elastomer is a matrixfor a hard-segment structure of the two sheets (11, 12).
 6. The emulatedwood as claimed in claim 4, wherein the thermoplastic elastomer at leastcomprises a first thermoplastic elastomer and a second thermoplasticelastomer, wherein the first thermoplastic elastomer and the secondthermoplastic elastomer are two thermoplastic elastomers with differentcharacteristics, and wherein the first thermoplastic elastomer is amatrix for a soft-segment structure of the two sheets (11, 12) and thesecond thermoplastic elastomer is a matrix for a hard-segment structureof the two sheets (11, 12).
 7. The emulated wood as claimed in claim 5,wherein the first thermoplastic elastomer is a polymer group of one orany mixture of styrene-butadiene-styrene block copolymer (SBS),styrene-isoprene-styrene block copolymer (SIS), and styrenic blockcopolymer (SBC) with a weight percentage of 10-80%, and wherein thesecond thermoplastic elastomer is a polymer group of one or any mixtureof polystyrene (PS), acrylonitrile-styrene copolymer (AS),acrylonitrile-butadiene-styrene (ABS), and high-impact polystyrene(HIPS) with a weight percentage of 10-80%.
 8. The emulated wood asclaimed in claim 6, wherein the first thermoplastic elastomer is apolymer group of one or any mixture of styrene-butadiene-styrene blockcopolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), andstyrenic block copolymer (SBC) with a weight percentage of 10-80%, andwherein the second thermoplastic elastomer is a polymer group of one orany mixture of polystyrene (PS), acrylonitrile-styrene copolymer (AS),acrylonitrile-butadiene-styrene (ABS), and high-impact polystyrene(HIPS) with a weight percentage of 10-80%.
 9. The emulated wood asclaimed in claim 7, wherein the foaming agent is an azo-based chemicalfoaming agent or a baking soda physical foaming agent with a weightpercentage of 0.1-15.0%, and wherein the crosslinking agent is dicumylperoxide, 2,5-(tert-butylperoxide)-2,5-dimethylhexane, or sulfur with aweight percentage of 0.01-2.0%.
 10. The emulated wood as claimed inclaim 8, wherein the foaming agent is an azo-based chemical foamingagent or a baking soda physical foaming agent with a weight percentageof 0.1-15.0%, and wherein the crosslinking agent is dicumyl peroxide,2,5-(tert-butylperoxide)-2,5-dimethylhexane, or sulfur with a weightpercentage of 0.01-2.0%.
 11. The emulated wood as claimed in claim 9,wherein the plurality of synthetic fibers (13) is glass fibers or carbonfibers.
 12. The emulated wood as claimed in claim 10, wherein theplurality of synthetic fibers (13) is glass fibers or carbon fibers. 13.The emulated wood as claimed in claim 1, wherein the two sheets (11, 12)further comprise foaming promotors, dyes, or fire retardants.